Brutus AAA全能型特种钢焊条
Shield Metal Arc Welding(SMAW - Stick)手工焊条电弧焊
For dissimilar and all categories of steel-tool, high alloy, nickel alloy, stainless, manganese and cast steels. 适用于工具钢、高合金钢、镍合金钢、不锈钢、锰钢和铸钢等所有类别钢间的焊接或异种焊接。
Features 功能
Strength 127,000psi/876MPa
抗拉强度高达127,000psi/876MPa
35% Elongation
35%伸长率
Excellent AC stability
卓越的交流稳定下
All positions
全位置焊接
Easy Strike and Restrike
轻松起弧和复弧
No Spatter / Easy Slag Release
无飞溅/易脱渣
Exceptional Smooth Bead
卓越平滑的焊道
Spray-Type Arc With Low Heat
低热喷涂式电弧
Excellent Undercoating/buildup For Hardfacing
出色的打底层，适用于堆焊
Wear and Shock Resistant
耐磨和抗冲击
Ideal For Dissimilar Steels
适用于异种钢
Ductile, Crack Resistant Deposit
韧性、抗裂熔敷层
Use for Broken Stud Extraction(See Thread Repair & Bolt Removal)
可用于拆除断裂螺栓（参见螺纹修理和螺栓拆卸）
Characteristics 特点
Brutus AAA has superior wear, shock and corrosion resistance and it can be used for joining dissimilar steels. In addition, Brutus AAA has a special flux coating that gives it superior operating characteristics, allowing the welder to produce an unusually strong, smooth weld deposit with minimum effort.
Brutus AAA具有优异的耐磨性、抗冲击性和耐腐蚀性，可用于连接异种钢。此外，Brutus AAA具有特殊的焊剂涂层，使其具有卓越的操作特性，使焊工能够以最小的努力产生异常坚固、光滑的焊缝熔覆层。
Brutus AAA’s ease of application makes it especially suitable where precise weld control and appearance are important. Thin sections and delicate parts can be repaired easily. It gives excellent results on dies, tools, molds, gears and exposed food handling equipment. Its high strength and ductility make it useful in almost all repairs of similar or dissimilar steels.
Brutus AAA的易用性使其特别适用于精确的焊接控制和外观非常重要的应用。薄的工件和脆弱的零件可以很容易地修复。它在模具、工具、铸模、齿轮和外露的食品处理设备上都能获得出色的效果。其高强度和延展性使其在几乎所有类似或不同钢的维修中都很有用。
Technical技术规格
Size and Amps AC/DC+(DCEP)
|
Inches |
3/32 |
1/8 |
5/32 |
|
(mm) |
(2.4) |
(3.2) |
(4.0) |
|
Amps |
45-85 |
65-125 |
85-155 |
Best Practices Application 应用
Clean weld area.
清洁焊接区域。
Bevel heavy sections.
对重型截面进行倒角。
Preheat high alloys and heavy sections to 400ºF (240ºC).
将高合金和重型型材预热至400ºF（240ºC）。
Use short arc.
使用短弧。
Tilt electrode 15º in direction of travel.
将焊条沿行驶方向倾斜15º。
For rapid filleting, increase amps and drag electrode at 45º.
为了快速嵌缝，提高电流并在45º下拖动焊条。
Remove slag between passes.
清除焊道之间的熔渣。